Effect of Laccol-modified Epoxy (Epolac) on Toughness of Epoxy ResinsN. H. Tran, V. D. Tran and H. T. Dang
View Abstract and References
ABSTRACTIn this study, a series of Laccol-modified epoxy (Epolac) was directly dispersed in the epoxy resin and then the modified matrices were cured with cyanethyldiethylenetriamine as a curing agent. Tension and critical stress intensity factor (KIC) measurements were performed in order to observe the effect of Laccol modification on the fracture properties of resin. Results showed an optimum concentration of Laccol (15 wt%) into epoxy matrix, which offered maximum toughening. Fractured surfaces of the specimens have been critically studied through scanning electron microscopic (SEM) analysis to gain insight into phase morphology. SEM photographs showed that phase separation did not occur in these cases because Laccol participated in epoxy polymer networks. Results obtained from dynamic mechanical thermal analysis showed that the glass transition temperatures of the epoxy resin matrix were slightly reduced on the addition of Laccol. The overall results showed that it was possible to obtain excellent impact strength and good mechanical properties with the use of Laccol as a toughness agent for the epoxy resins.View Full Article
Key words: Epoxy resin; Laccol-modified epoxy; fracture toughness; mechanical properties; Dynamic Mechanical Thermal Analysis
REFERENCESPascault, J.-P. and Williams, R.J.J. (2010) Epoxy Polymers: New Materials and Innovations, Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.Nakamura, Y., Yamaguchi, M., Okubo, M. and Matsumoto, T. (1992) Effect of particle size on the fracture toughness of epoxy resin filled with spherical silica, Polymer, 33, 3415–3426.Zamanian, M., Mortezaei, M., Salehnia, B. and Jam, J.E. (2013) Fracture toughness of epoxy polymer modified with nanosilica particles: particle size effect, Engineering Fracture Mechanics, 97, 193–206.Tripathi, G. and Srivastava, D. (2007) Effect of carboxyl-terminated poly(butadiene-co-acrylonitril) (CTBN) concentration on thermal and mechanical properties of binary blends of diglycidyl ether of bisphenol-A (DGEBA) epoxy resin, Materials Science and Engineering, A 443, 262–269.Wise, C.W., Cook, W.D. and A.A. Goodwin, A.A. (2000) CTBN rubber phase precipitation in model epoxy resins, Polymer, 41, 4625–4633. Chen, K. and Jan, Y.H. (1992) Fracture mechanism of toughened epoxy resin with bimodal rubber-particle size distribution, Journal of Materials Science, 27,111–121.Ratna, D. (2001) Phase separation in liquid rubber modified epoxy mixture: relationship between curing conditions, morphology and ultimate behavior, Polymer, 42, 4029–4218. Mimura, K., Ito, H. and Fujioka, K. (2001) Toughening of epoxy resin modified with in situ polymerized thermoplastic polymers, Polymer, 42, 9223–9233.Chikhi, N., Fellahi, S. and Bakar, M. (2002) Modification of epoxy resin using reactive liquid (ATBN) rubber, European Polymer Journal, 38, 251–264.Imanaka, M., Motohashi, S., Nishi, K., Nakamura, Y. and Kimoto, M. (2009) Crack-growth behaviour of epoxy adhesives modified with liquid rubber and cross-linked rubber particles under mode I loading, International Journal of Adhesion and Adhesives, 29, 45–55.Phai, L.T., Dieu,T.V. and Kim, T.N. (1996) Structures of Laccol: part 2-Structures of branching chains, Vietnamese Journal of Chemistry, 34, 56–62.Ngoc, P.T.M., Phuc, B.T. and Van, N.T.H. (2000) Synthesis and Application of Diethylenetriamine-acrylonitrile Adducts as Curing Agent for Epoxy Resin, Vietnamese Journal of Chemistry, 38(3), 45–49.ASTM D 5045-99 (1999). Standard test methods for plane-strain fracture toughness and strain energy release rate of plastic materials, American Society for Testing and Materials, PA 19428.Wise, C.W., Cook, W.D. and Goodwin, A.A. (1997) Chemico-diffusion kinetics of model epoxy-amine resins, Polymer, 38, 3251–3261.